低合金碳钢处于腐浊环境C4级下的涂层体系
发布时间:2014-12-04
低合金碳钢处于腐浊环境C4级下的涂层体系
底材:低合金碳钢
表面处理:锈浊等级为A.B.C的钢材,表面处理达Sa2.5级(参见ISO-8501-01)
体系编号 |
底涂层 |
后道涂层 |
涂层体系 |
预期耐久性 |
||||||
漆基类型 |
底漆类型a |
涂装道数 |
NDFTb um |
漆基类型 |
涂装道数 |
NDFTb um |
低 |
中 |
高 |
|
A4.01 |
AK |
Misc. |
1-2 |
80 |
AK |
3-5 |
200 |
|
|
|
A4.02 |
AK |
Misc. |
1-2 |
80 |
AY,PVC,CRc |
3-5 |
200 |
|
|
|
A4.03 |
AK |
Misc. |
1-2 |
80 |
AY,PVC,CRc |
3-5 |
240 |
|
|
|
A4.04 |
AY,CR,PVC |
Misc. |
1-2 |
80 |
AY,PVC,CRc |
3-5 |
200 |
|
|
|
A4.05 |
AY,CR,PVC |
Misc. |
1-2 |
80 |
AY,PVC,CRc |
3-5 |
240 |
|
|
|
A4.06 |
EP |
Misc. |
1-2 |
160 |
AY,PVC,CRc |
2-3 |
200 |
|
|
|
A4.07 |
EP |
Misc. |
1-2 |
160 |
AY,PVC,CRc |
2-3 |
280 |
|
|
|
A4.08 |
EP |
Misc. |
1 |
80 |
EP,PUR |
2-3 |
240 |
|
|
|
A4.09 |
EP |
Misc. |
1 |
80 |
EP,PUR |
2-3 |
280 |
|
|
|
A4.10 |
EP,PUR,ESId |
Zn(R) |
1 |
60e |
AY,PVC,CRc |
2-3 |
160 |
|
|
|
A4.11 |
EP,PUR,ESId |
Zn(R) |
1 |
60e |
AY,PVC,CRc |
2-4 |
200 |
|
|
|
A4.12 |
EP,PUR,ESId |
Zn(R) |
1 |
60e |
AY,PVC,CRc |
3-4 |
240 |
|
|
|
A4.13 |
EP,PUR,ESId |
Zn(R) |
1 |
60e |
EP,PUR |
2-3 |
160 |
|
|
|
A4.14 |
EP,PUR,ESId |
Zn(R) |
1 |
60e |
EP,PUR |
2-3 |
200 |
|
|
|
A4.15 |
EP,PUR,ESId |
Zn(R) |
1 |
60e |
EP,PUR |
3-4 |
240 |
|
|
|
A4.16 |
ESI |
Zn(R) |
1 |
60e |
------- |
1 |
60 |
|
|
|
底漆漆基 |
类型 |
水性好可能性 |
后道涂层漆基 |
类型 |
水性好可能性 |
AK=醇酸 |
单组份 |
可 |
AK=醇酸 |
单组份 |
可 |
CR=氯化橡胶 |
单组份 |
|
CR=氯化橡胶 |
单组份 |
|
AY=丙烯酸 |
单组份 |
可 |
AY=丙烯酸 |
单组份 |
可 |
PRV=氯化乙烯聚合物类 |
单组份 |
|
PRV=氯化乙烯聚合物类 |
单组份 |
|
EP=环氧 |
双组份 |
可 |
EP=环氧 |
双组份 |
可 |
ESI=硅酸乙酯 |
单组份和双组份 |
可 |
PUR=聚氨酯,脂肪族 |
单组份和双组份 |
可 |
PUR=聚氨酯,脂肪族或芳香族 |
单组份和双组份 |
可 |
|
|
|
a) Zn(R)=富锌底漆,Misc=采用其他类型防锈颜料的底漆,(参见5.2条)
b) NDFT=额定干膜厚度(更多信息参见5.4条)
c) 推荐与涂料生产商进行相容性确认
d) 推荐在硅酸锌底漆(ESI)上复涂一道后续涂层作为连接漆/过度漆
e) 选择富锌底漆,NDFT适宜选择范围为40-80um