发布时间:2014-12-04
低合金碳钢处于腐浊环境C5-1与C5-m级下的涂层体系
表面处理:锈浊等级为A.B.C的钢材,表面处理达Sa2.5级(参见ISO-8501-01)合金碳钢处于腐浊环境C5-1与C5-m级下的涂层体系
涂层体系编号 |
底涂层 |
后道涂层 |
涂层体系 |
预期耐久性 |
|||||||
漆基类型 |
底漆类型a |
涂装道数 |
NDFTb um |
漆基类型 |
涂装道数 |
NDFTb um |
低 |
中 |
高 |
||
C5-1 |
|||||||||||
A51.01 |
EP,PUR |
Misc. |
1-2 |
120 |
AY,PVC,CRc |
3-0 |
200 |
|
|
|
|
A51.02 |
EP,PUR |
Misc. |
1 |
80 |
EP,PUR |
3-4 |
320 |
|
|
|
|
A51.03 |
EP,PUR |
Misc. |
1 |
150 |
EP,PUR |
2 |
300 |
|
|
|
|
A51.04 |
EP,PURESId |
Zn(R) |
1 |
60e |
EP,PUR |
3-4 |
240 |
|
|
|
|
A51.05 |
EP,PURESId |
Zn(R) |
1 |
60e |
EP,PUR |
3-5 |
320 |
|
|
|
|
A51.06 |
EP,PURESId |
Zn(R) |
1 |
60e |
AY,PVC,CRc |
4-5 |
320 |
|
|
|
|
C5-M |
|||||||||||
A5M-01 |
EP,PUR |
Misc. |
1 |
150 |
EP,PUR |
2 |
300 |
|
|
|
|
A5M-02 |
EP,PUR |
Misc. |
1 |
80 |
EP,PUR |
3-4 |
320 |
|
|
|
|
A5M-03 |
EP,PUR |
Misc. |
1 |
400 |
------ |
1 |
400 |
|
|
|
|
A5M-04 |
EP,PUR |
Misc. |
1 |
250 |
EP,PUR |
2 |
500 |
|
|
|
|
A5M-05 |
EP,PURESId |
Zn(R) |
1 |
60e |
EP,PUR |
4 |
240 |
|
|
|
|
A5M-06 |
EP,PURESId |
Zn(R) |
1 |
60e |
EP,PUR |
4-5 |
320 |
|
|
|
|
A5M-07 |
EP,PURESId |
Zn(R) |
1 |
60e |
EPC |
3-4 |
400 |
|
|
|
|
A5M-08 |
EPC |
Misc. |
1 |
100 |
EPC |
3 |
300 |
|
|
|
|
底漆漆基 |
类型 |
水性化可能性 |
后道涂层漆基 |
类型 |
水性化可能性 |
EP=环氧 |
双组份 |
可 |
EP=环氧 |
双组份 |
可 |
EPC=环氧化合物 |
双组份 |
|
EPC=环氧化合物 |
双组份 |
|
ESI=硅酸乙酯 |
单组份和双组份 |
可 |
UR=聚氨酯,脂肪族 |
单组份和双组份 |
可 |
PUR=聚氨酯,脂肪族或芳香族 |
单组份和双组份 |
可 |
CP=氯化橡胶 |
单组份 |
|
|
|
|
AY=丙烯酸 |
单组份 |
可 |
|
|
|
PVC=氯化乙烯聚合物 |
单组份 |
|
a) Zn(R)=富锌底漆,Misc=采用其他类型防锈颜料的底漆,(参见5.2条)
b) NDFT=额定干膜厚度(更多信息参见5.4条)
c) 推荐与涂料生产商进行相容性确认
d) 推荐在硅酸锌底漆(ESI)上复涂一道后续涂层作为连接漆/过度漆
e) 选择富锌底漆,NDFT适宜选择范围为40-80um