热浸镀锌钢处于C2至C5-1与C5-M腐浊环境下的涂层体系
发布时间:2014-12-04
热浸镀锌钢处于C2至C5-1与C5-M腐浊环境下的涂层体系
基材:热浸镀锌钢材
ISO12944-4给出了一些表面处理的案例,表面处理方式与所用涂层体系有关,应按涂料制造商的要求进行。
涂层体系编号 |
底漆层 |
后道涂层 |
涂层体系 |
预期耐久值g (参见ISO12944-4中5.5条) |
|||||||||||||||||
漆基类型 |
涂层道数 |
NDFT umb |
基料类型 |
涂层道数 |
NDFT umb |
C2 |
C3. |
C4 |
C5-1 |
C5-M |
|||||||||||
L |
M |
H |
L |
M |
H |
L |
M |
H |
L |
M |
H |
L |
M |
H |
|||||||
A7.01 |
--- |
---- |
--- |
PVC |
1 |
80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.02 |
PVC |
1 |
40 |
PVC |
2 |
120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.03 |
PVC |
1 |
80 |
PVC |
2 |
160 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.04 |
PVC |
1 |
80 |
PVC |
3 |
240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.05 |
--- |
--- |
--- |
AY |
1 |
80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.06 |
AY |
1 |
40 |
AY |
2 |
120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.07 |
AY |
1 |
80 |
AY |
2 |
160 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.08 |
AY |
1 |
80 |
AY |
3 |
240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.09 |
--- |
---- |
---- |
EP,PUR |
1 |
80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.10 |
EP,PUR |
1 |
60 |
EP,PUR |
2 |
120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.11 |
EP,PUR |
1 |
80 |
EP,PUR |
2 |
160 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.12 |
EP,PUR |
1 |
80 |
EP,PUR |
3 |
240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A7.13 |
EP,PUR |
1 |
80 |
EP,PUR |
3 |
320 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
漆基类型 |
组份数量 |
水性化可能性 |
后道涂层漆基 |
组份数量 |
水性化可能性 |
AY=丙烯酸 |
单组份 |
可 |
AY=丙烯酸 |
单组份 |
可 |
PVC=氯化乙烯聚合物 |
单组份 |
|
PVC=氯化乙烯聚合物 |
单组份 |
|
EP=环氧 |
单组份和双组份 |
可 |
EP=环氧 |
单组份和双组份 |
可 |
PUR=聚氨酯,脂肪族或芳香族 |
双组份 |
可 |
PUR=聚氨酯,脂肪族 |
双组份 |
可 |
b NDFT=额定干膜厚度(更多信息参见5.4条)
g 在这种情况下,涂层体系的耐久性和涂层与热浸镀锌基材的附着力有关。